Evaluation of the shear bond strength of ceramic orthodontic brackets to glazed monolithic zirconia using different bonding protocols

Douara, Youmna; Abdul Kader, Sally; Kassem, Hassan; Mowafy, Mohamed

doi:10.21608/eos.2019.77627

Evaluation of the shear bond strength of ceramic orthodontic brackets to glazed monolithic zirconia using different bonding protocols

Document Type : Original Article

Authors

¹ Deparment of Orthodontics, Faculty of Dentistry, Alexandria University, Egypt

² Department of Dental Biomaterials, Faculty of Dentistry, Alexandria University, Egypt

³ Department of Orthodontics, Faculty of Dentistry, Alexandria University, Egypt

10.21608/eos.2019.77627

Abstract

Abstract
AIM: The aim of this study was to evaluate the shear bond strength (SBS) of ceramic brackets to glazed monolithic zirconia using three different bonding protocols.
MATERIALS AND METHODS: Forty-five monolithic glazed zirconia embedded into acrylic resin were randomly assigned to 3 groups (n = 15) following air abrasion by 50 μm aluminum oxide particles, the groups were treated with: (A) Assure Plus, (B) Silane + Assure Plus (C) Hydrofluoric acid + Silane + Transbond XT primer. Ceramic brackets were bonded to the zirconia discs using Transbond XT. Following thermocycling (500 cycles, 5° - 55° C), SBS, failure mode and Adhesive Remnant Index were assessed.
RESULTS:Group C showed the highest SBS followed by Group B with no statistically significant difference. Most of the specimens in Group C showed an adhesive failure between the bracket base and the adhesive, whereas Group B presented mainly a mixed cohesive adhesive failure. SBS in Group A was significantly lower than either groups showing an adhesive failure at the zirconia- adhesive interface.
CONCLUSIONS: Both Assure Plus + Silane and the classical ceramic bonding protocol achieved clinically acceptable SBS of ceramic brackets bonded to glazed zirconia. However, Assure Plus + Silane achieved better debonding characteristics.